What kind of material is 8620?
8620 is a low carbon nickel chromium molybdenum alloy steel with good carburized properties. The nickel content contributes to a high strength case toughness and above average core toughness. The chromium and molybdenum support the proper formation of carbides resulting in good surface hardness and wear.
Is 8620 a low alloy steel?
Overview. A medium-strength, low-carbon alloy steel, 8620 contains good toughness and strength properties, along with good core strength. 8620 has a high case toughness and above average core toughness due to the nickel content. Additionally, it is the most widely used carburizing alloy steel.
How strong is 8620 alloy steel?
The mechanical properties of annealed AISI 8620 alloy steel are outlined in the table below….Mechanical Properties.
|Tensile strength||530 MPa||76900 psi|
|Yield strength||385 MPa||55800 psi|
|Elastic modulus||190-210 GPa||27557-30458 ksi|
|Bulk modulus (typical for steel)||140 GPa||20300 ksi|
Will 8620 steel rust?
Besides, the 400°C tempered SAE 8620 steel is only susceptible to local attack of pitting corrosion and can exhibit an excellent corrosion resistance.
How hard is 8620 steel?
AISI 8620 Steel is a low alloy nickel, chromium, molybdenum case hardening steel, generally supplied in the as rolled condition with a maximum hardness HB 255max….8620 Steel Mechanical Properties.
|Hardness, Knoop (converted from Brinell hardness)||169||169|
Can you case Harden 8620?
HEAT TREATING 8620 can be hardened to 1500° F followed by water quench.
What is 8620 alloy steel?
Alloy Steel 8620, also sold as AISI 8620, is a hardenable, carburizing, low alloy steel. This alloy offers users outstanding flexibility, wear resistance, as well as ease of weldability through conventional methods. Leaders in a number of critical industries rely on Alloy Steel 8620 for important products and parts such as:
What is Sasae 8620 steel?
SAE 8620 is defined as low carbon alloy steel which has 0.5% Cr, 0.2% Mo and 0.5% Ni as strengthening alloy elements.It is generally supplied as annealed condition with hardness HB255max.
What is g86200 steel used for?
AISI SAE 8620 Steel (UNS G86200) AISI SAE 8620 steel is a commonly used low-alloy material for carburizing, with excellent carburizing response, good hardenability for most section sizes, it has many extensive applications due to its low cost, better machinability, and availability. SAE AISI 8620 Steel Properties
How do you heat carburize 8620 steel?
A common carburizing method of AISI SAE 8620 steel is to heat up to 925 °C (1700 °F) at a potential of 0.9% C in a prepared carbon-containing atmosphere, hold for about 4 hours (to reach a depth of 1.3 mm [0.050 in]), and reduce the temperature to 845 °C (1555 °F).